Name:  H62 brass rod
Model:  H62
Brand:  Brass category
Standard:  GB/T5231-2001
Description:

Executive Standard: H62 brass (GB / T5231-2001).

H62 brass represents an average copper content of 62% of the ordinary brass, adding other elements on the basis of ordinary brass called special brass copper alloy, is still "H", said back will add an element with other chemical symbol and average components, such as H62 for copper content of 60.5% ~ 63.5%, the balance being zinc content; and HAl59-3-2 indicates its copper content of 57% to 60%, an aluminum content of 2.5% to 3.5%, Ni content of 2% to 3%, the rest is zinc content brass is divided into ordinary brass, three special brass and cast brass, cast brass ZCu beginning to back with the other elements of symbols and their average content.

Features:
Ordinary brass, H62 (ie forty-six brass) has good mechanical properties, thermal state plastic, plastic cold state can, cutting good, easy brazing and welding, corrosion resistance, but easy to produce corrosion cracking. Is widely used an ordinary brass varieties. At room temperature β is much more rigid compared to α-phase, and thus can be used to withstand a greater load of parts. α + β two-phase brass can be thermally processed at above 600 ℃. α + β two-phase microstructure of brass: α solid solution for bright white, β is ordered CuZn-based solid solution.

Purpose:

Do all kinds of deep drawing and bending manufacturing force components, such as pins, rivets, washers, nuts, conduits ,, the barometer spring, screen, radiator parts.

Specifications:

Complete rods, plates, pipes and other specifications can be customized according to customer requirements.

The main physical parameters:
Density: 8.5g / cm ^ 3

Tensile strength: (σb / MPa) 410-630)

Hardness of 105 ~ 175 (HV)

Elongation (A%): 15.0

Properties Thickness: 0.3-10

Chemical composition:
Cu: 60.5-63.5, Ni: 0.5
Fe: 0.15
Pb: 0.08
Zn: margin
Impurities: 0.5